Izina | Uburemere bworoshye Alumina Amatafari | ||
LG-0.6 | LG-0.8 | LG-1.0 | |
Ubucucike bwinshi (g / cm3) | 0.6 | 0.8 | 1.0 |
Ubukonje bukonje (Mpa) ≥ | 1.9 | 2.9 | 4.0 |
Guhindura umurongo uhoraho 1300 ℃ * 12h (%) ≤ | 0.5 | 0.5 | 0.5 |
Ubushyuhe bwa Ubushyuhe Ubushyuhe Ubushyuhe 350 ± 25 ℃ W / (m · K) | ≤0.250 | ≤0.320 | ≤0.450 |
Kuvunika munsi yumutwaro 0.1Mpa (℃) ≥ | 1300 | 1350 | 1380 |
Al2O3 (%) ≥ | 50 | 52 | 52 |
Fe2O3 (%) ≤ | 1.8 | 1.6 | 1.5 |
Ubushyuhe bwa serivisi ntarengwa (℃) | 1300 | 1350 | 1380 |
Amatafari maremare ya alumina akoreshwa cyane mugukora amashyanyarazi yinganda imbere, nk'itanura riturika, itanura rishyushye, itanura ryamashanyarazi hejuru, reverberator, itanura rya sima nibindi. Byongeye kandi, amatafari maremare ya alumina nayo akoreshwa cyane nkamatafari yo kugenzura, guhagarika sisitemu ikomeza, amatafari ya nozzle, nibindi.